Default How to decap an IC

This is a collection of instructions from the web on decapping ICs. I have not successfully decapped any ICs yet, but when/if I do I will post my results.
Reply With Quote
  #2  
Old 09-05-2005, 01:51 PM
Grant Stockly Grant Stockly is offline
Administrator
 
Join Date: Jan 2005
Posts: 447
Default

From: Jon Hiller : hiller-at-anl.gov
Date: Thu, 24 Jan 2002 19:26:21 -0600
Subject: IC package removal

Contents Retrieved from Microscopy Listserver Archives
http://www.microscopy.com/Microscopy...yArchives.html

Body of Message



Does anybody have a chemical solution for removing IC packaging without
damaging the internal components? Simple grinding from the top down is not
suitable because I need all the interconnects intact. Any help in this
matter is greatly appreciated.

Sincere regards,

Jon Hiller
================================================== ================
Jon M. Hiller
Argonne National Laboratory
Materials Science Division
Electron Microscopy Center
Tel: 630-252-9558
Fax: 630-252-4798
Email: hiller-at-anl.gov
================================================== ================


From daemon Thu Jan 24 19:34:57 2002
Reply With Quote
  #3  
Old 09-05-2005, 01:53 PM
Grant Stockly Grant Stockly is offline
Administrator
 
Join Date: Jan 2005
Posts: 447
Default

From: Diane.Ciaburri-at-gd-ais.com
Date: Fri, 25 Jan 2002 08:50:58 -0500

Subject: Re: IC package removal (LONG)


Contents Retrieved from Microscopy Listserver Archives
http://www.microscopy.com/Microscopy...yArchives.html
Body of Message

Jon,

I assume you're speaking about plastic packages since you want a chemical removal technique. Below your message is a summary of responses that I received when I asked a similar question. I can't comment on them, because my project dried up after I asked the question and I never got to try any of the techniques, but there look like some good ones.

Diane Ciaburri
General Dynamics
Pittsfield, MA


<Note from logjam, the following posts until noted by me are a part of this e-mail. I'm separating them for readability. I'm also fixing the line break issues that make the post very hard to read and doing some minor formatting>

Last edited by Grant Stockly; 09-05-2005 at 02:09 PM.
Reply With Quote
  #4  
Old 09-05-2005, 02:10 PM
Grant Stockly Grant Stockly is offline
Administrator
 
Join Date: Jan 2005
Posts: 447
Default

<Part of the last post>

Here's the summary (long) for all those interested in deencapsulating plastic encapsulated ICs. I have no preferences as I haven't tried any yet, but thought the fuming sulfuric acid might be 'fun'. Thanks again!
Reply With Quote
  #5  
Old 09-05-2005, 02:11 PM
Grant Stockly Grant Stockly is offline
Administrator
 
Join Date: Jan 2005
Posts: 447
Default

<Part of the previous post>

-- [ From: Garber, Charles A. * EMC.Ver #3.1 ] --
Hi Diane,

The way this is generally done is to mill the plastic down on a grinding wheel to the point where only a fairly thin layer of plastic remains.

Then, using a plasma etcher, and a mixture of oxygen to CF4 (for example, 30% oxygen/70% CF4), whereby the oxygen etches away the plastic and the CF4 etches away the glass frit that is usually found in the plastic, you can remove the remaining plastic (package) without damaging the device itself. Different people like to use different gas ratios, of course, and that is probably a function, at least to some degree, of the concentration of glass frit in their particular plastic.


The SPI Plasma Prep II unit, as shown on URL http://www.2spi.com/catalog/instruments/etchers1.html in the world, is probably the most widely used unit for doing this type of operation. It is inexpensive and highly reliable, and requires virtually no maintenance.

Chuck
Reply With Quote
  #6  
Old 09-05-2005, 02:12 PM
Grant Stockly Grant Stockly is offline
Administrator
 
Join Date: Jan 2005
Posts: 447
Default

<Part of the previous post>

The ion beam approach works well. I have not used it recently on finer pitch ICs. With as-built feature sizes of 2-4u, it is fine. It will stop at the passivation and leave the Al bond wires intact. The resulting package looks like it has a V-shaped pit in it (which it does). The extent of the pit depends on the size of the die and if you want to blast down to the lead frame or substrate.

I have not done this on finer pitch devices. I would be a bit skeptical about these mostly because of the smaller bond pads. The etching would still stop at the passivation.

There are numerous places in Silicon Valley that do this on an outsource basis. Typical costs are about $75 per IC. I can get some contacts for you if you'd like.

gary g.
Reply With Quote
  #7  
Old 07-25-2008, 10:19 PM
erik@nisene.com erik@nisene.com is offline
Junior Member
 
Join Date: Jul 2008
Posts: 2
Default You need decap equipment

Decapping by hand is not only extremely dangerous, but it is done successfully by very few people. Nisene Technology Group Manufactures the equipment you would need to do this. Email me at erik@nisene.com and I will set you up with a quote and resources on getting out equipment.
Reply With Quote
  #8  
Old 07-26-2008, 09:52 AM
Grant Stockly Grant Stockly is offline
Administrator
 
Join Date: Jan 2005
Posts: 447
Default

The hard part is getting acid good enough. After an hour of work with some over-the-counter nitric acid I had a 68000 done, but the water content was so high that it left a residue on the chip. Its still fun to look at. MEFAS at $35-40 is worth it for sure!
Reply With Quote
  #9  
Old 05-15-2009, 06:16 PM
elrob1981 elrob1981 is offline
Junior Member
 
Join Date: May 2009
Posts: 1
Default Sulfuric and Nitric Acid concentrations for we chemical decapsulation

Guys,

I just joined this forum and would really appreicate your help here.

What are the concentrations of the sulfuric and nitric acids you use for
wet chemical decapsulation. I'm in the process of purchasing chemicals for our chemical lab and need to know the concentration of acid in the solution that will yield the best results. I was thinking 90% Nitric Acid and 96% sulfuric acid would be ok to use but need you to confirm.

thank you

Roberto
Reply With Quote
  #10  
Old 09-18-2009, 06:52 PM
erik@nisene.com erik@nisene.com is offline
Junior Member
 
Join Date: Jul 2008
Posts: 2
Default

Quote:
Originally Posted by elrob1981 View Post
Guys,

I just joined this forum and would really appreicate your help here.

What are the concentrations of the sulfuric and nitric acids you use for
wet chemical decapsulation. I'm in the process of purchasing chemicals for our chemical lab and need to know the concentration of acid in the solution that will yield the best results. I was thinking 90% Nitric Acid and 96% sulfuric acid would be ok to use but need you to confirm.

thank you

Roberto

There are several variations of sulfuric and nitric acid on the market. Our equipment uses 20% fuming sulfuric and 98% fuming nitric. I could give you a few pointers if you would like to discuss further. erik@nisene.com or 831-761-7980
Reply With Quote
Reply

Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump

Similar Threads
Thread Thread Starter Forum Replies Last Post
Decapping IC with copper bond wire. chandan_ug Electronics 0 10-08-2010 07:40 AM
IC 4449 confirmation bugman Altair 680 1 06-17-2008 03:20 AM
Netherlands + IC99 Architect Kenbak-1 5 10-13-2007 06:41 AM
Decapping an IC Grant Stockly Electronics 0 01-28-2005 10:21 AM


All times are GMT. The time now is 10:42 PM.


Powered by vBulletin® Version 3.8.9
Copyright ©2000 - 2024, vBulletin Solutions, Inc.